Influence of Waste Tire Particles on Freeze–Thaw Resistance and Impermeability Performance of Waste Tires/Sand-Based Autoclaved Aerated Concrete Composites

Waste tires/sand-based autoclaved aerated concrete (SAAC) composites were prepared by mixing waste tires, which have different particle sizes and content. The physical performance, mechanical properties, freeze–thaw resistance, impermeability performance, phase composition, and microstructure of waste tires/sand-based autoclaved aerated concrete composite materials were examined. The results demonstrated that the 750-μm-sized waste tire particles on the surface of the SAAC composite did not agglomerate. Moreover, these particles did not damage the pore structure of the composites. The SAAC composites, with a relatively high compressive strength and low mass-loss rate, were obtained when the contents of waste tire particles ranged from 1.0 to 2.5 wt.%. For composites prepared with 2.0 wt.% of 750-μm-sized waste tire particles, the optimal compressive and flexural strength values were 3.20 and 0.95 MPa, respectively. The increase in the rate of water absorption on SAAC composites was lowest (i.e., 16.3%) when the soaking time was from 24 to 120 h.

Dieses Werk wurde unter der Creative-Commons-Lizenz Namensnennung 4.0 International (CC-BY 4.0) veröffentlicht und darf unter den Lizenzbedinungen vervielfältigt, verbreitet, öffentlich zugänglich gemacht, sowie abgewandelt und bearbeitet werden. Dabei muss der Urheber bzw. Rechteinhaber genannt und die Lizenzbedingungen eingehalten werden.