Fiber Showdown: A Comparative Analysis of Glass vs. Polypropylene Fibers in Hot-Mix Asphalt Fracture Resistance

Autor(en):

ORCID
ORCID
Medium: Fachartikel
Sprache(n): Englisch
Veröffentlicht in: Buildings, , n. 9, v. 14
Seite(n): 2732
DOI: 10.3390/buildings14092732
Abstrakt:

Cracks in asphalt mixtures compromise the structural integrity of roads, increase maintenance costs, and shorten pavement lifespan. These cracks allow for water infiltration, accelerating pavement deterioration and jeopardizing vehicle safety. This research aims to evaluate the impact of synthetic fibers, specifically glass fiber (GF) and polypropylene fiber (PPF), on the crack resistance of Hot-Mix Asphalt (HMA). An optimal asphalt binder content of 5% was used in all sample designs. Using the dry mixing technique, GFs and PPFs were incorporated into the HMA at dosages of 0.50%, 1.00%, and 1.50% by weight of the aggregate. The effects of these fibers on the mechanical fracture properties of the HMA were assessed using Semi-Circular Bending (SCB), Indirect Tensile Asphalt Cracking Tests (IDEAL-CTs), and Three-Point Bending (3-PB) tests. This study focused on fracture parameters such as fracture work, peak load, fracture energy, and crack indices, including the Flexibility Index (FI) and Crack Resistance Index (CRI). The results from the SCB and IDEAL-CT tests showed that increasing GF content from 0.5% to 1.5% significantly enhances the flexibility and crack resistance of HMA, with FI, CRI, and CT Index values increasing by 247.5%, 55%, and 101.35%, respectively. Conversely, increasing PPF content increases the mixture’s stiffness and reduces its crack resistance. The PP-1 mixture exhibited higher FI and CT Index values, with increases of 31.1% and 10%, respectively, compared to the PP-0.5 mixture, based on SCB and IDEAL-CT test results. The SCB, IDEAL-CT, and 3-PB test results concluded that fibers significantly influence the fracture properties of bituminous mixtures, with a 1% reinforcement dosage of both PPFs and GFs being optimal for enhancing performance across various applications.

Copyright: © 2024 by the authors; licensee MDPI, Basel, Switzerland.
Lizenz:

Dieses Werk wurde unter der Creative-Commons-Lizenz Namensnennung 4.0 International (CC-BY 4.0) veröffentlicht und darf unter den Lizenzbedinungen vervielfältigt, verbreitet, öffentlich zugänglich gemacht, sowie abgewandelt und bearbeitet werden. Dabei muss der Urheber bzw. Rechteinhaber genannt und die Lizenzbedingungen eingehalten werden.

  • Über diese
    Datenseite
  • Reference-ID
    10799833
  • Veröffentlicht am:
    23.09.2024
  • Geändert am:
    23.09.2024
 
Structurae kooperiert mit
International Association for Bridge and Structural Engineering (IABSE)
e-mosty Magazine
e-BrIM Magazine