Experimental Study on the Mechanical Properties of Steel Fiber Ferronickel Slag Powder Concrete

The use of ferronickel slag powder (FNSP) as a cementitious additional material has been supported by numerous reports. FNSP concrete has the same shortcomings as ordinary concrete, including low hardness. In this study, in order to make FNSP concrete more durable, end-hooked type steel fibers were incorporated. To understand how various elements affect the mechanical properties of steel fibers, an experiment was carried out on the mechanical properties of steel FNSP concrete (SFNSPC). FNSP’s principal ingredients, with a particle size distribution ranging from 0.5 to 100 μm and a sheet-like powder shape, are CaO, SiO2, Al2O3, MgO, and others, according to tests conducted on the material’s microstructure and composition. Then, eighteen mix proportions were developed, comprising six distinct FNSP replacement rate types and three distinct steel fiber content types. Crucial metrics were evaluated and analyzed, including the relationship among the toughness, tensile strength, and compressive strength as well as slump, splitting tensile strength, compressive strength, and uniaxial compressive stress–strain curve of SFNSPC. The results showed that the slump of SFNSPC under different FNSP replacement rates decreased with increasing steel fiber volume. Steel fibers have a small but positive effect on SFNSPC’s compressive strength; nonetheless, as FNSP replacement rates increased, SFNSPC’s slump gradually decreased, though not by much. These results show that FNSP is a viable alternative cementitious material in terms of strength. Specifically, the splitting tensile strength of SFNSPC improves with an increase in steel fiber content, and the pace at which SFNSPC strength drops with an increase in the FNSP replacement rate. With varying mix proportions, the stress–strain curve trend of SFNSPC remains mostly constant, and steel fibers improve the compressive toughness of SFNSPC. After adding 0.5% and 1.0% steel fibers, the toughness index of concrete with different FNSP replacement rates increased by 8–30% and 12–43%, respectively.

Dieses Werk wurde unter der Creative-Commons-Lizenz Namensnennung 4.0 International (CC-BY 4.0) veröffentlicht und darf unter den Lizenzbedinungen vervielfältigt, verbreitet, öffentlich zugänglich gemacht, sowie abgewandelt und bearbeitet werden. Dabei muss der Urheber bzw. Rechteinhaber genannt und die Lizenzbedingungen eingehalten werden.