Evaluation of Strengths from Cement Hydration and Slag Reaction of Mortars Containing High Volume of Ground River Sand and GGBF Slag

This paper investigates the cement hydration, and the slag reaction contributes to the compressive strengths of mortars mixed with ground river sand (GRS) and ground-granulated blast furnace (GGBF) slag with different particle sizes. GRS (inert material) and GGBF slag (reactive material) were ground separately until the median particle sizes of 32 ± 1, 18 ± 1, and 5 ± 1 micron and used to replace Portland cement (PC) in large amount (40–60%) by weight of the binder. The results showed that, at the early age, the compressive strength obtained from the cement hydration was higher than that obtained from the slag reaction. The results of compressive strength also indicated that the GGBF slag content and particle size play important roles in the slag reaction at the later ages, whereas cement hydration is more prominent at the early ages. Although the results could be expected from the use of GGBF slag to replace PC in mortar or concrete, this study had presented the values of the compressive strength along with ages and the finenesses of GGBF slag that contributed from cement hydration and from GGBF slag reaction.

Dieses Werk wurde unter der Creative-Commons-Lizenz Namensnennung 4.0 International (CC-BY 4.0) veröffentlicht und darf unter den Lizenzbedinungen vervielfältigt, verbreitet, öffentlich zugänglich gemacht, sowie abgewandelt und bearbeitet werden. Dabei muss der Urheber bzw. Rechteinhaber genannt und die Lizenzbedingungen eingehalten werden.