Effect of Rubber Aggregates on Early-Age Mechanical Properties and Deformation Behaviors of Cement Mortar

Rubberized cement-based materials are widely utilized because of their good ductility, impact resistance, and fatigue resistance. This research investigated the effect of the rubber aggregates content, particle size of rubber aggregates, and water–cement ratio on the early-age mechanical properties and deformation behaviors of mortar through laboratory tests, and strength reduction coefficient fitting models were established according to the testing results. The results show that the compressive strength growth rate of cement mortar is about 15% slower than that of flexural strength. The existence of rubber aggregates lowers the strength increase rate of mortar. The reduction coefficient of strength decreases with increasing rubber aggregates content and increases with the age of mortar. Increasing rubber aggregates content and decreasing particle size of rubber aggregate can lower the autogenous shrinkage in the initial stage, but the autogenous shrinkage of the later stage increases as the rubber aggregates content increases, with a turning point between 30 h and 50 h. After 3 days, the dry shrinkage of mortar accounts for about 70–80% of the total shrinkage, and it increases with higher rubber aggregate content, smaller particle size of rubber aggregates, and higher water–cement ratios.

Dieses Werk wurde unter der Creative-Commons-Lizenz Namensnennung 4.0 International (CC-BY 4.0) veröffentlicht und darf unter den Lizenzbedinungen vervielfältigt, verbreitet, öffentlich zugänglich gemacht, sowie abgewandelt und bearbeitet werden. Dabei muss der Urheber bzw. Rechteinhaber genannt und die Lizenzbedingungen eingehalten werden.