The Effect of Red Mud Content on the Compressive Strength of Geopolymers under Different Curing Systems

To maximize the utilization of red mud in geopolymers, a red mud–metakaolin (RM-MK) geopolymer and red mud–fly ash (RM-FA) geopolymer were prepared, respectively. The effects of red mud content on the compressive strength and microstructure of the geopolymers were investigated under three different curing conditions. The results showed that the strength of the geopolymer decreased linearly with an increase in the red mud content, whether curing at room temperature or 80 °C. Surprisingly, curing in an autoclave, the appropriate amount of red mud had a favorable impact on the mechanical properties of the geopolymers. When the amount of red mud was 50%, the strength of the RM-MK geopolymer reached its highest compressive strength, 36.3 MPa, and the strength of the RM-FA geopolymer reached its highest at 31.7 MPa. Compared with curing at low temperature, curing the red mud-based geopolymers under a higher temperature and higher pressure can maximize the use of red mud. XRD analysis indicated that zeolite minerals formed. The SEM results showed that the geopolymers cured in an autoclave had a dense structure.

Dieses Werk wurde unter der Creative-Commons-Lizenz Namensnennung 4.0 International (CC-BY 4.0) veröffentlicht und darf unter den Lizenzbedinungen vervielfältigt, verbreitet, öffentlich zugänglich gemacht, sowie abgewandelt und bearbeitet werden. Dabei muss der Urheber bzw. Rechteinhaber genannt und die Lizenzbedingungen eingehalten werden.