Durability of Structural Lightweight Concrete Containing Expanded Perlite Aggregate

This study focuses on the development of durable structural lightweight concrete(LWC) by incorporating expanded perlite aggregate (EPA) in the range of 0 to 20% by weight. In order to ensure ist durability when exposed to chloride environment, concrete was produced with low water-to-cement ratio and ordinary Portland cement (OPC) was replaced with 50% and 7% ground granulated blast furnace slag (GGBFS) and silica fume (SF), respectively. The mechanical properties and durability of concrete were assessed by determining the unit weight, compressive strength, flexural strength, drying shrinkage, chloride permeability and migration, as well as resistance of concrete to corrosion of reinforcing steel. Very importantly, thermal insulation properties were determined using a hot guarded plate. In addition, a finite element model (FEM) was prepared to study the behavior of EPA-modified concrete under seismic loading. The results showed that the unit weight of concrete was reduced by 20% to 30% when compared with the normal weight concrete (NWC). The compressive strength of the developed LWC was sufficient to be used as structural concrete, particularly of those mixtures containing 10% and 15% perlite aggregate. The durability of LWC was comparable to NWC in terms of chloride diffusion and resistance of concrete to corrosion of reinforcing steel. The tangible outcomes also include the superior thermal insulation properties of LWC compared to NWC. The greater incorporation of EPA in the concrete resulted in better behavior under seismic loading.

Dieses Werk wurde unter der Creative-Commons-Lizenz Namensnennung 4.0 International (CC-BY 4.0) veröffentlicht und darf unter den Lizenzbedinungen vervielfältigt, verbreitet, öffentlich zugänglich gemacht, sowie abgewandelt und bearbeitet werden. Dabei muss der Urheber bzw. Rechteinhaber genannt und die Lizenzbedingungen eingehalten werden.