Bonded Behavior of Hybrid-Bonded CFRP to Heat-Damaged Concrete Interface

The reliable bond of CFRP to heat-damaged concrete is fundamental to ensuring cooperative working when the CFRP is applied for strengthening fire-damaged concrete structures. In this paper, the bond performance of hybrid-bonded (HB) CFRP to a heat-damaged concrete surface was investigated by using single shear tests. The concrete blocks were initially heat-damaged to temperatures of 100 °C, 200 °C, 300 °C, and 400 °C. The heat-damaged blocks were subsequently bonded with CFRP using the HB technique. The primary experiment parameters were the exposure temperature, the number of mechanical fasteners, and the bonded layers of CFRP. The test results show that the external-bonded (EB) and HB-CFRP joints with concrete exposed to a temperature of 400 °C were prone to fail with concrete shear-tension due to the decreased shear strength of concrete at high temperatures. The EB- and HB-CFRP joints with heat-damaged concrete anchored with no more than three fasteners present a higher bond than the reference joints with unheated concrete, while the HB-CFRP joints anchored with three fasteners provide a decreased bond capacity with the increase in exposure temperature. The utilization rate of single-layer CFRP joints with unheated concrete increased by 57.9%, 139.5%, and 136.8% with the mechanical fasteners in numbers of one, two, and three compared with the reference specimen. Accordingly, the bond capacity increased by 111.8%, 128.4%, and 186.7%. Finally, a model was proposed to estimate the bond strength of HB-CFRP joints with heat-damaged concrete.

Dieses Werk wurde unter der Creative-Commons-Lizenz Namensnennung 4.0 International (CC-BY 4.0) veröffentlicht und darf unter den Lizenzbedinungen vervielfältigt, verbreitet, öffentlich zugänglich gemacht, sowie abgewandelt und bearbeitet werden. Dabei muss der Urheber bzw. Rechteinhaber genannt und die Lizenzbedingungen eingehalten werden.