Autogenous Deformation of Alkali-Activated Blast Furnace Slag Concrete Subjected to Variable Curing Temperatures

Deformations of alkali-activated slag concrete (AASC) with high MgO and Al₂O₃content, subjected to variable curing temperature were studied. Sodium silicate and sodium carbonate were used as alkali activators. The obtained results showed development of deformations consisting of both shrinkage and expansion. Shrinkage appeared not to be affected by the activator type, while the expansion developed after the cooling down phase in stabilized isothermal conditions and did not stop within the duration of the tests. X-ray diffraction analysis performed shortly after the cooling down phase indicated the formation of crystalline hydrotalcite, which was associated with the observed expansion. A mixture with a higher amount of sodium silicate showed less expansion, likely due to the accelerated hydration and geopolymerization leading to the increased stiffness of the binder matrix.

Dieses Werk wurde unter der Creative-Commons-Lizenz Namensnennung 4.0 International (CC-BY 4.0) veröffentlicht und darf unter den Lizenzbedinungen vervielfältigt, verbreitet, öffentlich zugänglich gemacht, sowie abgewandelt und bearbeitet werden. Dabei muss der Urheber bzw. Rechteinhaber genannt und die Lizenzbedingungen eingehalten werden.