Effect of Warm-Mix Agent EC-120 on Performance of Asphalt Binder and Its Microscopic Mechanism

In order to figure out the influence of the warm-mix agent EC-120 on the performance of the asphalt binder and its micro mechanism in warm-mixing process, a matrix asphalt, A-70, and SBS-modified asphalt, SBS I-D, were modified with different contents of EC-120, respectively. Then, conventional macromechanic performance tests, dynamic shear rheological (DSR) test at high-temperature, and bending beam rheological (BBR) test at low-temperature were carried out on asphalt binder samples. Meanwhile, they were microscopically analyzed through Fourier transform infrared spectrometer (FTIR) and differential scanning calorimeter (DSC). The results indicated that EC-120 can reduce the viscosity of asphalt binder at high temperature. With the increase of EC-120 content, the high-temperature rutting resistance of two kinds of warm-mix asphalt (WMA) increased, but their crack resistance at low-temperature was reduced. FTIR indicated that this is due to the generation of oxides containing carbonyl functional groups after EC-120 was blended with asphalt binder. The DSC endothermic curves of WMA binders are obviously different from those of base binders, and a strong endothermic peak appears in the interval of 102°C–113°C, indicating that EC-120 will endothermically melt at the temperature of 102°C∼113°C, so it can play the role in reducing the viscosity of asphalt binder at the range of construction temperatures.

This creative work has been published under the Creative Commons Attribution 4.0 International (CC-BY 4.0) license which allows copying, and redistribution as well as adaptation of the original work provided appropriate credit is given to the original author and the conditions of the license are met.